Product Parameters
| Properties | unit | WD-XD20FZ-J | WD-XD10 FZ-J | WD-XD20 FZ-JY | WD-XD20 FZ-JN |
| The highest working temperature of conductor | ℃ | 125 | 125 | 105 | 105 |
| Original strength at break | MPa | 11.5 | 11 | 11.6 | 11.8 |
| Original elongation at break | % | 220 | 250 | 200 | 198 |
| Air thermal aging | ℃/h | 158℃;168h | 158℃;168h | 135℃;168h | 135℃;168h |
| Tensile strength variation after aging | % | 9 | 11 | 13 | 10.5 |
| Elongation at break variation after aging | % | -10 | -15 | -14 | -14 |
| Hot set test condition(200℃;15min;0.2MPa) |
| Hot elongation | % | 70 | 70 | 75 | 75 |
| Permanent deformation after cooling |
| 0 | 0 | 0 | 0 |
| Brittle temperature with low temperature | -40℃ | PASS | PASS | PASS | PASS |
| 20℃ Volume resistivity | Ω ·m | 5×1012 | 5×1012 | 3.5×1012 | 3.5×1012 |
| Oxygen Index | % | 32 | 32 | 30 | 30 |
| Smoke density | Flaming mode | 70 | 70 | 85 | 85 |
| Non-flaming mode | 150 | 160 | 170 | 175 |
| Corrosivity of gases |
| PH |
| 5.6 | 5.8 | 5.4 | 5.3 |
| Conductivity | us/mm | 0.8 | 0.9 | 0.8 | 0.8 |
| Density | g/cm³ | 1.41 | 1.41 | 1.42 | 1.42 |
Note: The above data are typical values of our company's products, not as standard assessment values of products.
Packing
Net weight 25kg: Inner aluminum foil/polyethylene composite film bag, outer kraft paper composite bag.
Net weight 1000kg: Inner aluminum foil/polyethylene composite film bag, outer polypropylene woven composite bag.
Storage
The product should be stored in a clean, dry and ventilated warehouse, and should not be damaged by sun, rain, water and other abnormal conditions. Storage temperature should not be lower than 0℃. The storage period of the product shall not exceed 6 months from the date of production.