Product Parameters
| Performance | Unit | LDPE | LLDPE | MDPE | HDPE |
| The highest working temperature | ℃ | 70 | 70 | 80 | 80 |
| MFR(melt flow rate) | g/10min | 0.3 | 0.8 | 1 | 0.2 |
| Density | g/cm³ | 0.93 | 0.93 | 0.95 | 0.97 |
| Original strength at break | MPa | 15 | 16 | 19 | 22 |
| Original elongation at break | % | 600 | 600 | 660 | 680 |
| Brittle temperature with low temperature | -76℃ | PASS | PASS | PASS | PASS |
| ESCR F/500h | F₀、h | PASS | PASS | PASS | PASS |
| 200℃ Oxidation induction period | min | 40 | 45 | 48 | 50 |
| Carbon Black Content | % | 2.61 | 2.7 | 2.56 | 2.53 |
| Carbon Black Dispersion | level | 2 | 2 | 2 | 2 |
| Vicat softening temperature | ℃ | 一 | 一 | 110 | 110 |
| Air thermal aging(100℃;240h) |
| Tensile strength variation after aging | MPa | 14 | 15 | 18 | 21 |
| Elongation at break variation after aging | % | 500 | 550 | 580 | 680 |
| Dielectric strength | kv/mm | 28 | 28 | 28 | 28 |
| 20℃ Volume resistivity | Ω ·m | 1.5×10¹⁴ | 1.5×10¹⁴ | 1.5×10¹⁴ | 1.5×10¹⁴ |
| Dielectric constant |
| 一 | 一 | 2.2 | 2.15 |
Note:
1.The above data are typical values of our company's products, not as standard assessment values of products.
2.We can increase the rodent and ant proof performance of the product according to customer reguirements.
Packing
Net weight 25kg: Inner aluminum foil/polyethylene composite film bag, outer kraft paper composite bag.
Net weight 1000kg: Inner aluminum foil/polyethylene composite film bag, outer polypropylene woven composite bag.
Storage
The product should be stored in a clean, dry and ventilated warehouse, and should not be damaged by sun, rain, water and other abnormal conditions. Storage temperature should not be lower than 0℃. The storage period of the product shall not exceed 6 months from the date of production.