Product Parameters
| Properties | Unit | WD-XD20 FZ | WD-XD10
FZ-2 | WD-XD20 FZ-FZH | WD-XD20 FZ-FZHZ |
| The highest working temperature of conductor | ℃ | 125 | 125 | 105 | 105 |
| Original strength at break | MPa | 13 | 12.8 | 12.6 | 12.4 |
| Original elongation at break | % | 218 | 220 | 210 | 209 |
| Air thermal aging | ℃/h | 158℃;168h | 158℃;168h | 135℃;168h | 135℃;168h |
| Tensile strength variation after aging | % | 10 | 9.5 | 8.5 | 8.9 |
| Elongation at break variation after aging | % | -13 | -11 | -12 | -13 |
| Hot set test condition(200℃;15min;0.2MPa) |
| Hot elongation | % | 60 | 60 | 70 | 70 |
| Permanent deformation after cooling |
| 0 | 0 | 0 | 0 |
| Brittle temperature with low temperature | -40℃ | PASS | PASS | PASS | PASS |
| 20℃ Volume resistivity | Ω ·m | 2×1011 | 3×1011 | 1.5×1011 | 1.5×1011 |
| Oxygen Index | % | 36 | 35 | 36 | 36 |
| Smoke density | Flaming mode | 86 | 85 | 91 | 87 |
| Non-flaming mode | 178 | 150 | 180 | 182 |
| Corrosivity of gases |
| PH |
| 5.4 | 5.6 | 5.3 | 5.3 |
| Conductivity | us/mm | 0.8 | 0.9 | 0.9 | 0.7 |
| Density | g/cm³ | 1.48 | 1.46 | 1.47 | 1.47 |
Note: The above data are typical values of our company's products, not as standard assessment values of products
Packing
Net weight 25kg: Inner aluminum foil/polyethylene composite film bag, outer kraft paper composite bag.
Net weight 1000kg: Inner aluminum foil/polyethylene composite film bag,outer polypropylene woven composite bag.
Storage
The product should be stored in a clean,dry and ventilated warehouse,and should not be damaged by sun rain, water and other abnormal conditions. Storage temperature should not be lower than 0℃. The storage period of the product shall not exceed 6 months from the date of production.